Brazing Alloys For Copper And Copper Based
Bezeichnung Products References |
Zusammensetzung /Composition in Gew. % | Schmelzbereich Melting Range °C | Arbeitstemp. Working |
Dichte Density |
Zugfestigkeit Tensile Strength |
Internernationale Normen / International Norms |
||||||
Ag | Cu | P | Others | AWS A5.8 | EN 1044 | DIN 8513 | EN 17672 | |||||
MTL 95 | - | 95 | 5 | - | 710-920 |
|
8,2 | 250 | - | - | - | - |
MTL 94 | - | 94 | 6 |
|
710-880 |
|
8,1 | 250 | - | CP 203 | L-CuP6 | CuP 179 |
MTL 93 | - | 93 | 7 |
|
710-820 |
|
8,1 | 250 | BCup-2 | CP 202 | L-CuP7 | CuP 180 |
Nano MTL 93 | - | 93 | 7 |
|
710-820 |
|
8,1 | 250 | BCup-2 | CP 202 | L-CuP7 | CuP 180 |
MTL 7Sn7 | - | 86 | 7 | Sn 7 | 645-695 |
|
8 | 250 | - | CP 302 | - | CuP 386 |
MTL92 | - | 92 | 8 |
|
710-750 |
|
8 | 250 | - | CP 201 | L-CuP8 | CuP 182 |
Nano MTL 92 | - | 92 | 8 |
|
710-750 |
|
8 | 250 | - | CP 201 | L-CuP8 | CuP 182 |
MTL X1A | 0,4 | 93,6 | 6 |
|
710-740 |
|
8,1 | 250 | - | - | - | - |
MTL X1 | 1 | 92,5 | 6,5 |
|
645-810 |
|
- | 8,1 | - | - | - | - |
Nano MTL1 | 1 | 92,5 | 6,5 |
|
645-810 |
|
- | 8,1 | - | - | - | - |
MTL X2 | 2 | 91,8 | 6,2 |
|
645-800 |
|
8,1 | 250 | BCup-6 | CP 105 | L-Ag2P | CuP 279 |
Nano MTL 2 | 2 | 91,8 | 6,2 |
|
645-800 |
|
8,1 | 250 | BCup-6 | CP 105 | L-Ag2P | CuP 279 |
MTL X5 | 5 | 88,8 | 6,2 |
|
645-810 |
|
8,2 | 250 | BCup-3 | CP 104 | L-Ag5P | CuP 281 |
Nano MTL 5 | 5 | 88,8 | 6,2 |
|
645-810 |
|
8,2 | 250 | BCup-3 | CP 104 | L-Ag5 | CuP 281 |
MTL 15 | 15 | 80 | 5 |
|
645-800 |
|
8,4 | 250 | BCup-5 | CP 102 | L-Ag15 P | CuP 284 |
Nano TA 15 | 15 | 80 | 5 |
|
645-800 |
|
8,4 | 250 | BCup-5 | CP 102° | L-Ag15P | CuP 284 |